EL SC Plate 4.0x4.0mm, 0.50mm thick
Quantum / Radiation DetectorsSingle Crystal
Single Crystal Electronic (ELSC) grade is Element Six's highest purity CVD diamond material with respect to point defects, with the lowest N and NV centre density of our commercially available materials. This material contains less than 5 ppb (often below 1 ppb) Nitrogen concentration and typically has less than 0.03 ppb NV concentration
It has shown great versatility as a spin host for a range of quantum applications from magnetic field sensing to quantum information processing, and as a good base material for applications where the defect or colour centre used is the negatively charged nitrogen-vacancy centre (NV-).
Its combined Electron Mobility, Radiation Hardness and Charge Collection Efficiency of >99% make it the ideal radiation detection material
Plates are supplied with high quality, low damage polished surfaces in sizes of 2x2, 4x4 and 4.5x4.5 mm in thickness of 500 microns
- Carat Weight EA: 0.17 ct
- Crystallographic Orientation (Miscut): +/-3°
- Crystallography: Typically 100% single sector {100}
- Lateral Dimensions Measured: to smaller side
- Edges: Laser Cut
- Edge Features: < 0.2 mm
- Edge Orientation: <110> edges
- Face Orientation: {100} faces
- Laser Kerf: <5°
- Lateral Tolerance: +0.2/-0 mm
- Length: 4.0 mm
- Side 1, Roughness, Ra: polished, Ra<5nm on {100} face
- Side 2, Roughness, Ra: polished, Ra<5nm on {100} face
- Thickness Tolerance: +/- 0.05 mm
- Thickness Dimension: 0.50 mm
- Width: 4.0 mm
- Boron Concentration [B]: <1 ppb
- Charge Collection Efficiency (CCE): Typically >95%
- Charge Collection Distance (CCD): Typically >475µm, @0.5 V µm-1 applied field, for 500 µm plate
- Nitrogen Concentration: [Ns0] < 5 ppb (Typically <1)