EL SC Plate 2.0x2.0mm, 0.50mm thick

Quantum / Radiation DetectorsSingle Crystal
In stock
£695.00

5

SKU
145-500-0385
EL SC Plate 2.0x2.0x0.5mm

Single Crystal Electronic (ELSC) grade is Element Six's highest purity CVD diamond material with respect to point defects, with the lowest N and NV centre density of our commercially available materials. This material contains less than 5 ppb (often below 1 ppb) Nitrogen concentration and typically has less than 0.03 ppb NV concentration

It has shown great versatility as a spin host for a range of quantum applications from magnetic field sensing to quantum information processing, and as a good base material for applications where the defect or colour centre used is the negatively charged nitrogen-vacancy centre (NV-).

Its combined Electron Mobility, Radiation Hardness and Charge Collection Efficiency of >99% make it the ideal radiation detection material

Plates are supplied with high quality, low damage polished surfaces in sizes of 2x2, 3x3 and 4.5x4.5 mm in thickness of 300 and 500 microns

  • Carat Weight EA: 0.03 ct
  • Crystallographic Orientation (Miscut): +/-3°
  • Crystallography: Typically 100% single sector {100}
  • Lateral Dimensions Measured: to smaller side
  • Edges: Laser Cut
  • Edge Features: < 0.2 mm
  • Edge Orientation: <110> edges
  • Face Orientation: {100} faces
  • Laser Kerf: <5°
  • Lateral Tolerance: +0.2/-0 mm
  • Length: 2.0 mm
  • Side 1, Roughness, Ra: polished, Ra<5nm on {100} face
  • Side 2, Roughness, Ra: polished, Ra<5nm on {100} face
  • Thickness Tolerance: +/- 0.05 mm
  • Thickness Dimension: 0.50 mm
  • Width: 2.0 mm
  • Boron Concentration [B]: <1 ppb
  • Charge Collection Efficiency (CCE): Typically >95%
  • Charge Collection Distance (CCD): Typically >475µm, @0.5 V µm-1 applied field, for 500 µm plate
  • Nitrogen Concentration: [Ns0] < 5 ppb (Typically <1)