EL SC Plate 2.0x2.0mm, 0.50mm thick

Quantum / Radiation DetectorsSingle Crystal
In stock
$865.00

10

SKU
145-500-0385
EL SC Plate 2.0x2.0x0.5mm

Single Crystal Electronic (ELSC) grade is Element Six's highest purity CVD diamond material with respect to point defects, with the lowest N and NV centre density of our commercially available materials. This material contains less than 5 ppb (often below 1 ppb) Nitrogen concentration and typically has less than 0.03 ppb NV concentration

It has shown great versatility as a spin host for a range of quantum applications from magnetic field sensing to quantum information processing, and as a good base material for applications where the defect or colour centre used is the negatively charged nitrogen-vacancy centre (NV-).

Its combined Electron Mobility, Radiation Hardness and Charge Collection Efficiency of >99% make it the ideal radiation detection material

Plates are supplied with high quality, low damage polished surfaces in sizes of 2x2, 4x4 and 4.5x4.5 mm in thickness of 500 microns

  • Carat Weight EA: 0.03 ct
  • Crystallographic Orientation (Miscut): +/-3°
  • Crystallography: Typically 100% single sector {100}
  • Lateral Dimensions Measured: to smaller side
  • Edges: Laser Cut
  • Edge Features: < 0.2 mm
  • Edge Orientation: <110> edges
  • Face Orientation: {100} faces
  • Laser Kerf: <5°
  • Lateral Tolerance: +0.2/-0 mm
  • Length: 2.0 mm
  • Side 1, Roughness, Ra: polished, Ra<5nm on {100} face
  • Side 2, Roughness, Ra: polished, Ra<5nm on {100} face
  • Thickness Tolerance: +/- 0.05 mm
  • Thickness Dimension: 0.50 mm
  • Width: 2.0 mm
  • Boron Concentration [B]: <1 ppb
  • Charge Collection Efficiency (CCE): Typically >95%
  • Charge Collection Distance (CCD): Typically >475µm, @0.5 V µm-1 applied field, for 500 µm plate
  • Nitrogen Concentration: [Ns0] < 5 ppb (Typically <1)